黑色類ABS樹脂材料,為光固化工藝打印的樹脂材料,具備樹脂材料的尺寸成型好,表面光滑的特點(diǎn),同時熱變形耐溫可以達(dá)到70到75度,韌性和強(qiáng)度比普通白色樹脂要好,可以進(jìn)行直接攻絲。顏色為黑色,不需要噴漆,為材料顏色需要黑色的手板客戶提供了更多的選擇。
MEASUREMENT測試項(xiàng)目
TEST METHOD 測試方法
VALUE 數(shù)值
90-minute UV post-cure 90分鐘紫外固化
Hardness 硬度, Shore D
ASTM D 2240
78~88
Flexural modulus 彎曲模量, Mpa
ASTM D 790
2,722-2,792
Flexural strength 彎曲強(qiáng)度, Mpa
ASTM D 790
69- 76
Tensile modulus 拉伸模量, MPa
ASTM D 638
2,649-2,731
Tensile strength 拉伸強(qiáng)度, MPa
ASTM D 638
41-58
Elongation at break 斷裂延長率
ASTM D 638
7 -11%
Poisson`s Ratio泊松比
ASTM D 638
0.4-0.44
Impact strength notched Izod, J/m
缺口沖擊強(qiáng)度
ASTM D 256
29 - 34
Heat deflection temperature, ℃
熱變形溫度
ASTM D 648 @66PSI
58~69
Glass transition,Tg
玻璃化轉(zhuǎn)變溫度,℃
DMA,E”peak
62~75
Coefficient of thermal expension,熱膨脹系數(shù), /℃
TMA(T<Tg)
90~103*E-6
Density 密度, g/cm3
1.12~1.18
Dielectric Constant介電常數(shù)
60 Hz
ASTM D 150-98
4.2~5.0
Dielectric Constant介電常數(shù)
1 kHz
ASTM D 150-98
3.3~4.2
Dielectric Constant介電常數(shù)
1 MHz
ASTM D 150-98
3.2~4.0
Dielectric Strength絕緣強(qiáng)度
kV/mm
ASTM D 1549-97a
12.8~16.1